Description
ADVANTAGES:
- Reduce carbon formation and the risk of explosion, and increase safety
- Virtually eliminate varnish and sludge deposits, ensuring that items such as oil/air separators in rotary. Compressors function efficiently at all times.
- Provide better demulsibility, which is needed for rapid and complete water separation (this is particularly important for oil flooded compressors, where condensate can accumulate in oil receivers)
- Extend oil drainage intervals up to 8000 hours or 12 month’s operations.
- Outstanding operating temperatures range which will affect operating economics in compressor down time and lubricant utilization. Good compatibility with elastomers used as seals in reciprocating compressors.
- Reduce oil consumption and carry over by virtue of their low volatility and good lubrication properties.
- Maintain the high efficiency of reciprocating compressors by significantly reducing valve deposits.
- Reduce maintenance costs by reducing wear and deposits associated with the use of mineral oils, savings on replacement parts and labour can be achieved.
- Improve oil receiver and crankcase performance by virtue of their low foaming properties.
PROPERTIES:
| ISO GRADE | 22 | 32 | 46 | 68 | 150 | 220 | 220 |
| Viscosity cSt @ 40°C (ASTM D-445) | 22 | 30.8 | 45.6 | 65.8 | 147 | 221 | 318 |
| Viscosity cSt @ 100°C (ASTM D-445) | 4.8 | 6.1 | 8 | 10.6 | 19.2 | 24.6 | 33.8 |
| Viscosity Index (ASTM D-2270) 100 | 149 | 149 | 149 | 149 | 149 | 149 | 149 |
| Flash Point °F/°C (ASTM D-92) 560°/294° | 230 | 235 | 240 | 240 | 265 | 265 | 265 |
| Fire Point °F/°C (ASTM D-92) 610°/321° | 264 | 282 | 284 | 284 | 315 | 315 | 315 |
| Pour Point °F/°C (ASTM D-92) -22°/-30° | -52 | -40 | -36 | -30 | -28 | -28 | -24 |
| Demulsibility ml. | 40/40/0 | 40/40/0 | 40/40/0 | 40/40/0 | 40/40/0 | 40/40/0 | 40/40/0 |
| Neutralization Number mg / KOH/g | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
| Foaming sequence 1 tendency/ stability ml. | 20/0 | 20/0 | 20/0 | 20/0 | 20/0 | 20/0 | 20/0 |
| Evaporation loss 22 hours at 149°C. % | 0.6 | 0.6 | 0.6 | 0.6 | 0.6 | 0.6 | 0.6 |
| Specific gravity at 25°C. | 0.942 | 0.942 | 0.942 | 0.942 | 0.972 | 0.972 | 0.972 |
| Conradson carbon deposits % Part 1:after aging without Fo2os% | 0.05 | 0.05 | 0.05 | 0.05 | 0.09 | 0.09 | 0.09 |
| Part 2: after aging with Fo2o3 (Pneurop) % | 2.5 | 2.5 | 2.5 | 2.5 | 2.4 | 2.4 | 2.4 |
| 4 ball wear test (40 kg.load for 1 hour )-scar diameter mm | 0.92 | 0.92 | 0.92 | 0.92 | 0.88 | 0.88 | 0.88 |
| Weld load kg | 135 | 135 | 135 | 135 | 140 | 140 | 140 |